On November 1, 2008, at approximately 1630 eastern daylight time, a Piper PA-44-180, registration N2214N, was substantially damaged when its nose landing gear collapsed during landing at Gwinnett County Airport (LZU), Lawrenceville, Georgia. The instructional flight was conducted under 14 Code of Federal Regulations Part 91 in day visual meteorological conditions. No flight plan was filed. The certificated flight instructor and commercial-rated student were not injured. The flight originated from LZU at 1530.
Flight Details
The student was performing a practice ILS approach as part of his multi-engine training program. After confirming "gear down, three green, nose gear in mirror," a normal touchdown was performed with no apparent side drift. As the nose was lowered to the runway, the nose gear collapsed. The airplane came to a stop on the runway, and the pilots exited the airplane normally.
Aircraft and Maintenance
An inspector from the Federal Aviation Administration inspected the aircraft and reported that the nose gear drag link bolt, Piper part number 402 940, failed. According to the airplane maintenance logbook, the bolt was installed on June 9, 2007. At the time of the accident, the airplane had accrued approximately 441 hours since the bolt was installed. Two new bearings associated with the bolt were also installed.
Piper Service Bulletin (SB) number 1156, dated April 7, 2005, applies to this airplane. The SB provides instructions for replacing the nose gear drag link bolt at 500-hour intervals. SB 1156 states that by design, the bolt is free to rotate inside a set of bushings, and over extended operating hours, rotation can generate score marks, causing stress concentrations. Left uncorrected, this condition could eventually result in bolt failure with subsequent nose gear collapse.
According to a representative from Piper, SB 1156 has not been incorporated into the PA-44-180 Aircraft Maintenance Manual (AMM) for this serial-numbered airplane. The SB has been incorporated for serial numbers 4496001 and higher. Piper expected the SB to be incorporated into the AMM for older aircraft in early 2010.
Examination of the Failed Bolt
The failed bolt was forwarded to the NTSB Materials Laboratory for examination. Examination of the accident bolt, using two exemplar bolts provided by Piper for comparison, revealed that the accident bolt met design specifications for hardness, surface roughness, and microstructure.
Further examination revealed that the bolt failed due to reversed bending fatigue. This is evidenced by diametrically opposed fatigue cracks that terminate at an area of overload fracture towards the middle of the bolt's cross-section. The central overload fracture region roughly corresponds to the neutral axis of the reversed bending force on the bolt. The bolt failed due to the merging of numerous fatigue cracks from many fatigue initiation points around the periphery of the bolt shank.